PHOENIX

• Formulation without BPA, BisGMA, TEGDMA and with no addition of HEMA
• High flexural strength >110 MPa.
• Extremely reduced inhibition oxygen layer: the surface of the cured material is almost dry.
• Aesthetic.
• Easy and fast to use.
• with remarkably high mechanical properties
• To make temporary crowns and long temporary bridges, with a pre-impression (indirect method).

Indication

To make temporary crowns and long temporary bridges, with a pre-impression (indirect method).

Composition

Glass fillers - Hydrophilic di-methacrylate resins modified urethane di-methacrylate resin - Catalysts - Stabilizers - Additives – Pigments.

Temporary C&B (Indirect Method)

1.Take a pre-operative impression. Interdental spaces should be rid of silicone material. 2. Remove and discard the used mixing tips and attach a new one on the cartridge. Insert the cartridge into the dispensing gun. 3. Blow dry impression and fill the concerned teeth area, with Phoenix. Always fill from the bottom up, until the impression is ¾ full. It is recommended to also inject some resin into the sulcus of the concerned teeth, with a yellow intra-oral tip, to avoid any lack of product, at the limits of the temporary crown. 4. Place the impression back in patient’s mouth and allow Phoenix MD to set undisturbed for about 40/45 seconds. 5. Remove the impression tray from mouth. At that stage, the material will be somehow flexible and will pull over any undercuts or non-parallel preparations. The material will fully cure in 2 additional minutes. 6. Remove the temporary crown or bridge from the impression and trim excesses. 7. Remove the smear layer from the surface (if any) by whipping with a cloth moistened with alcohol. 8. Polish and cement the temporary crown with a temporary cement (e.g.: Seal Temp or Seal Temp S).

Includes

PH-50-A1 50ml cartridge (75g), shade A1 + 10 mixers